ASP2595
PERFLEX
Odorless Polyaspartic Polyurea Elastic Waterproof Coating - ASP2595 is an advanced waterproof coating composed primarily of aspartate resin, along with pigments, fillers, and a minor quantity of low-odor solvents and additives. The varnish version of this product does not contain fillers. The coating is cured using a modified isocyanate, ensuring robust and reliable performance.
MAIN FEATURES
Excellent resistance to yellowing
Good adhesion to most substrates
High solid content, green and eco-friendly
Excellent elongation at break and tensile strength
APPLICATION LAYERS
ASP2595 Polyaspartic polyurea elastic waterproof coating: A coating layer that provides superior waterproof capability.
EPR3101 Solvent-Free Epoxy Primer (0.15-0.2mm): A base layer that ensures strong adhesion to the concrete.
Concrete: The foundational layer of the flooring system.
APPLICATION SCENARIOS
Odorless Polyaspartic Polyurea Elastic Waterproof Coating ASP2595, specifically designed for waterproofing concrete or tile base surfaces, is particularly apt for exterior wall waterproof repairs. Additionally, it's well-suited for applications like: pool and deck areas, bathrooms and kitchens, balconies and terraces, roofing projects, etc.
PHYSICAL PARAMETERS
Main Agent | Curing Agent |
Appearance: All colors liquid | Appearance: Colorless or slightly yellow transparent liquid |
Flash point (℃): 68 | Flash point (℃): 90 |
Specific gravity (g/cm3): 1.03±0.03 | Specific gravity (g/cm3): 1.1±0.05 |
| Viscosity (initial mixing at 25°C): 700-1000CPS | |
| Weight solids (A/B mix): 95±2% | |
| Gloss: Semi-gloss or glossy | |
| Coating film thickness: Dry film: 100-150 Wet film: 110-170μm | |
| Theoretical coating rate: | |
| Theoretical value: 9.5 square meters/Kg/100μm | |
Actual value: related to surface treatment, external environment, construction method and other factors | |
Material properties after curing | |
Elongation | ≧200% |
Tensile strength | ≧10MPa |
Tear strength N/mm | ≧40 |
Adhesion (concrete): | ≧4 MPa |
| Wear resistance (750g/500r,mg): | ≦25 |
Construction Parameters:
Use ratio:
A:B = 1: 1 mass ratio（please stir well before use）
Application time:
Temperature（℃） | 5 | 10 | 20 | 25 |
Pot life (mins) | 120 | 90 | 60 | 40 |
Construction conditions:
Ambient temperature: 5℃-30 ℃, Ambient humidity: ≤85%
Substrate temperature: must be greater than the air dew point temperature 3 ℃ or more.
Construction method: Brush, Roller or Spray
Cleaning agent: polyaspartic polyurea standard thinner
Drying time and painting interval:
| 5 | 10 | 20 | 30 |
Dry to the touch (hrs) | 3.5 | 3 | 2.5 | 2 |
| Dry to handle (hrs) | 15 | 12 | 10 | 8 |