ASP2530
PERFLEX
Polyaspartic Waterproof Elastic Middle Coat-ASP2530 is an odorless, high solid elastic waterproof coating with aspartate resin, pigments, and a polyether modified isocyanate curing agent. This solvent-free formula offers strong adhesion and durability for concrete substrates, ideal for waterproofing and anti-corrosion in basements, bridges, and more. It also works well on foam, plastic, and other substrates, providing a versatile protective solution.
MAIN FEATURES
Solvent-free product, environmentally friendly
Low odor and good workability
Thick film construction is possible, and one film formation is larger than 500μm
Excellent adhesion to concrete substrates
Excellent elongation at break and tensile strength
Simple construction and quick drying
APPLICATION LAYERS
ASP1475 Wear Resistant Polyaspartic (0.1mm): A topcoat layer providing high resistance to wear and tear for a durable finish.
ASP100 Polyaspartic Middle Coat (0.15-0.2mm): An intermediate layer designed to offer additional protection and bond strength between the topcoat and base layers.
ASP2530 Polyaspartic Sanded Coat (0.6-0.8mm): A textured coating infused with sand particles to enhance grip and durability against abrasion.
EPR3101 Solvent Free Epoxy Primer (0.15-0.2mm): A foundational layer that ensures strong adhesion to the concrete substrate.
Concrete: The solid base material which provides structural support for the coating system.
APPLICATION SCENARIOS
Polyaspartic Waterproof Elastic Middle Coat - ASP2530 is an odorless, high solid elastic waterproof coating with aspartate resin, pigments, and a polyether modified isocyanate curing agent. This solvent-free formula offers strong adhesion and durability for concrete substrates, ideal for waterproofing and anti-corrosion in basements, bridges, and more. It also works well on foam, plastic, and other substrates, providing a versatile protective solution.
PHYSICAL PARAMETERS
Main Agent | Curing Agent |
Appearance: All colors liquid | Appearance: All colors liquid |
Flash point (℃): 95 | Flash point (℃): 93 |
Specific gravity (g/ml): 1.45±0.05(A) | Specific gravity (g/ml): 1.06±0.05(B) |
| Mixing specific gravity (g/ml): 1.22±0.05 | |
| Weight solids (A/B mix): 95±2% | |
| Gloss: Bright | |
| Coating film thickness: Dry film: 500-600 Wet film: 510-610μm | |
| Theoretical coating rate: | |
| Theoretical value: 1.23kg/mm/m2 | |
Actual value: related to surface treatment, external environment, construction method and other factors | |
Material properties after curing | |
Elongation | ≧300% |
Tensile strength | 10-13MPa |
Tear strength N/mm | ≧55 |
Adhesion (concrete): | ≧2.5 MPa |
| Low temperature bendability (-35℃) | no cracks |
| Hardness (Shore A): | ≧ 85 |
Construction Parameters:
Brushing: A:B = 1: 0.8 mass ratio（please stir well before use）
Application time:
Temperature（℃） | 5 | 10 | 20 | 30 |
Pot life (mins) | 80-90 | 60-80 | 40-60 | 30-40 |
Construction conditions:
Ambient temperature: 5℃-30 ℃, Ambient humidity: ≤85%(RH)
Substrate temperature: must be greater than the air dew point temperature 3 ℃ or more.
Cleaning agent: epoxy thinner
Drying time and painting interval:
| 5 | 10 | 20 | 30 |
Dry to touch (hrs) | 4 | 3 | 2 | 1.5 |
Dry to handle (hrs) | 20 | 15 | 12 | 10 |
Dry to recoat (hrs) | 20 | 15 | 12 | 10 |
CLICK HERE TO DOWNLOAD TDS&MSDS