ASP2583-001
PERFLEX
Polyaspartic Polyurea High Solids Waterproof Coat-ASP2583-001 is a high-performance coating crafted with polyaspartic resin, complemented by a variety of pigments, fillers, auxiliary agents, and solvents. Its curing agent, a polyether modified isocyanate, not only contributes to its exceptional weather resistance but also enhances its superior waterproofing capabilities.
MAIN FEATURES
Solvent-free product, environmentally friendly
Thick film construction is possible, and one film formation is larger than 500μm
Excellent adhesion to concrete substrates
Premium elongation at break and tensile strength
Simple construction and quick drying
APPLICATION LAYERS
ASP2583-001 Polyaspartic Polyurea High Solids Waterproof Coat 0.1mm: A top coat layer that provides superior waterproofing capability.
EPR3101 Solvent-Free Epoxy Primer (0.15-0.2mm): A base layer that ensures strong adhesion to the concrete.
Concrete: The foundational layer of the flooring system.
APPLICATION SCENARIOS
Polyaspartic Polyurea High Solids Waterproof Coat-ASP2583-001 is primarily intended for waterproofing and anti-corrosion treatment of concrete substrates. It's ideal for use in various settings, including basements, bridges, roofs, and warehouses, as well as water parks. Additionally, its compatibility with foam, plastic, and other substrates makes it a versatile choice for a wide range of protective coating applications.
PHYSICAL PARAMETERS
Main Agent | Curing Agent |
Appearance: All colors liquid | Appearance: All colors liquid |
Flash point (℃): 70 | Flash point (℃): 51 |
Weight solids (A/B mix): ≥95% | |
| Viscosity: 1500-3000CPS (25℃, two-component mixing) | |
| Specific gravity (A/B mix): 1.1±0.05g/cm3 | |
| Gloss: high gloss | |
| Coating film thickness: Dry film: 500-600 Wet film: 560-680μm | |
| Theoretical coating rate: | |
| Theoretical value: 1.8 square meters/Kg/500μm | |
Actual value: related to surface treatment, external environment, construction method and other factors | |
Material properties after curing | |
Elongation | ≧300% |
Tensile strength | ≧15MPa |
Tear strength N/mm | ≧60 |
Adhesion (concrete): | ≧4 MPa |
| Wear resistance (1000g/500r): | ≦40 |
Construction Parameters:
Use ratio:
A:B = 1: 1 mass ratio（please stir well before use）
Application time:
Temperature（℃） | 5 | 10 | 20 | 25 |
Mix-use period(min) | 80-90 | 60-80 | 40-60 | 30-40 |
Construction conditions:
Ambient temperature: 5℃-30 ℃, Ambient humidity: ≤85%
Substrate temperature: must be greater than the air dew point temperature 3 ℃ or more.
Construction method: Brush, Roller or Spray
Cleaning agent: polyurea standard thinner
Drying time and painting interval:
| 5 | 10 | 20 | 30 |
Dry to the touch (hrs) | 3 | 2.5 | 2 | 1.5 |
Shiatsu drying (hrs) | 12 | 10 | 8 | 6 |
Re-coating Time(hrs) | 12 | 10 | 8 | 6 |
CLICK HERE TO DOWNLOAD TDS&MSDS