ASP110
PERFLEX
100% Solid Content Polyaspartic Flake Flooring ASP110 is made of two component aliphatic polyaspartic resin and isocyanate hardener, it has perfect visual appeal and durability, such as commercial environments, can be used effectively as a mid-coat or topcoat on flake and ultra-wear-resistant flooring. It is also highly resistant to UV rays, ensuring the coating retains its appearance and performance even with prolonged sun exposure. The solid content is pretty high.
MAIN FEATURES
Eco-Friendly High in solids and low in VOCs, non toxic.
Durability Excellent compressive strength and impact resistance, withstanding heavy loads without damage.
No Yellowing Remain its color for over 20 years under sun exposure.
APPLICATION LAYERS
ASP1375P Clear Wear Resistant Polyaspartic (0.1mm): A top layer for protection against wear and UV rays.
ASP110 Polyaspartic Middle Coat (0.15-0.2mm): This middle layer bonds with the flakes and supports the top layer, adding to the floor's durability.
Flake or quartz
ASP110 Polyaspartic middle coat 0.15-0.2m：This layer can bond the flake or quartz firmly.
EPR3101 Solvent-Free Epoxy Primer (0.15-0.2mm): A base layer that ensures strong adhesion to the concrete.
Concrete: The foundational layer of the flooring system.
APPLICATION SCENARIOS
Polyaspartic Flake Flooring ASP110 is particularly well-suited for flake flooring systems and ultra-wear-resistant surfaces, ideal for areas requiring both aesthetic qualities and high durability: Parking lots, Retail stores, Warehouses, Industrial factories, Garages, High-end showrooms, Galleries, Schools, Hospitals, Food service areas.
PHYSICAL PARAMETERS
Main Agent | Curing Agent |
Appearance: Colorless transparent liquid | Appearance: All colors liquid |
Viscosity 25℃: 400MPaS | Viscosity 25℃: 100MPaS |
Specific gravity 25°C: 1.02 | Specific gravity 25°C: 1.01 |
Solids: 78% | Solids: 96% |
Material properties after curing | |
Paint appearance | normal |
7 days hardness | shore D 68 |
Abrasion (CS17 wheel 750g, 500 rpm) | 25mg |
Elongation at break (%) | 15 |
Tensile strength (MPa) | 23 |
Concrete adhesion (Mpa) | 2.2 |
Impact resistance (1000g, 1m) | Pass |
Construction Parameters:
Use ratio:Roll coating: A: B = 1:1 mass ratio
Application time:
Temperature（℃） | 10 | 20 | 30 |
Pot life (mins) | 40 | 30 | 20 |
Construction conditions:
Ambient temperature: 0℃-35 ℃, Ambient humidity: ≤85%
Substrate temperature: must be greater than the air dew point temperature 3 ℃ or more.
Cleaning agent: polyaspartic polyurea standard thinner
Drying time and painting interval:
| 25 |
Open for pedestrian traffic (hrs) | 3 |
Open for vehicle traffic (days) | 7 |
Dry to recoat (hrs) | 3 |